POLYETHYLENE HM-CRP100-Black
HM-CRP100 Black is a black pipe grade resin (PE100) which is manufactured by suspension polymerization of
ethylene monomer, HM-CRP100 Blue is a bi-modal high density polyethylene with 1-Butene as comonomer.
Technical Data
HDPE: HMCRP100N Black (PE100 Black)
Characteristic Properties
Black PE100 resin
Density: 0.955-0.959 g/cm3
Main Applications
Top quality PE100 pressure
Pipes for gas and water transportaion
at higher pressures or with thinner
walls as PE8O
Density: 0.946-0.950 g/cm3
Additives
Antioxidant/Process stabilizer
Lubricant (processing aid)/ acid scavenger
Related products
POLYETHYLENE 0035
HB0035 is a high molecular weight high density polyethylene blow moulding grade combining blow
moulding extrusion behavior and superior mechanical properties. Blow moulded items made from HB
0035 exhibit high impact strength and good stress cracking resistance and high stiffness. HB 0035
contains antioxidant to protect the polymer from degradation during processing.
HB 0035 is a highly crystalline, non-polar thermoplastic and has excellent chemical resistance and
superb impact resistance at ambient conditions and even at cold temperatures.
POLYETHYLENE LL-0209-AA
"LL 0209AA" is a LLDPE copolymer with butene as
comonomer which contains antioxidant.
It is recommended for general purpose applications.
It is suitable for blending with conventional LDPE.
Film made from pure LL 02090 AA has the following
advantages over conventional LDPE:
Better sealing.higher puncture resistance.
Greater drawdown capability.
Higher tensile strength.
Neutralizer: Calcium Stearate.
Antioxidant: Irganox1010, Irganox168
POLYPROPYLENE Z-30-s
Z30S is widely used for the production of bulked continuous filament for carpet face yarns. Another major application is the production of high tenacity continuous filament for straps for backpacks, handles for big bags and safety belts. Continuous filament with medium tenacity is used for upholstery, sportswear and heavy duty clothing. Moplen Z 30 S is al also suitable for the production of low denier staple fibres for thermobonding.